FIMFLEX V3 V4 PV3 PV4
SRPS U.M3.231
Applied refiners, like APP and different
co-polymers, give these membranes good steadiness to cold and heat, a wide scope of applicability and good UV-stability. The
membranes are manufactured with inserts of reinforced glass voal (V) which provides optimal dimensional stability, or with
reinforced polyester material (PV) which ensures excellent mechanical characteristics and good dimensional stability
to the product. Surface of the membrane is protected with plastic foil.
Membranes with reinforced polyester material insert are characterized by high tearing resistance
and therefore they are especially suitable for waterproofing of flat roofs with mechanical
fixing in areas exposed to strong winds.
FIMFLEX membranes with protection of natural shale (Š) are used as final self-protective membranes
for sloped and flat inaccessible roofs. |
|
|
|
|
Characteristic |
Unit |
FIMFLEX V3 |
FIMFLEX V4 |
FIMFLEX PV3 |
FIMFLEX PV4 |
|
Length |
m |
10 |
7,5 |
10 |
7,5 |
|
Width |
cm |
100 |
100 |
100 |
100 |
|
Mass per unit area |
g/m² |
2.900 |
4.000 |
3.000 |
4.100 |
|
Binder content |
g/m² |
2.000 |
2.800 |
2.000 |
2.800 |
|
Thickness |
mm |
2,6 |
3,5 |
2,7 |
3,6 |
|
Tensile strength |
longitudinal |
N/5
cm |
300 |
350 |
400 |
400 |
| transversal |
N/5
cm |
200 |
250 |
300 |
300 |
| Elongation at break |
longitudinal |
% |
2 |
2 |
35 |
35 |
| transversal |
% |
2 |
2 |
35 |
35 |
|
Flow resistence at elevated temperature |
ºC |
+120 |
+120 |
+120 |
+120 |
|
Flexibility at low temperature |
ºC |
-5 |
-5 |
-5 |
-5 |
|
   |
|
|
 |